Abstract: The Taixi anthracite was used as the raw materials, and mixed with different masses of additives, namely silicon oxide, titanium oxide, and iron oxide, to prepare the coal-based graphite by high temperature graphitization. The microstructure of coal-based graphite was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), laser confocal Raman spectroscopy (Raman) and Specific surface area and porosity analyzer.The results show that the graphitization degree of the coal-based graphite can reach over 89% after high temperature heat treatment at 2800 °C , which significantly improves the microcrystalline structure of anthracite and achieves orderly rearrangement of sp² hybrid carbon atoms in the coal. Under the same additive mixing level, the graphitization degree and stacking height of coal-based graphite with titanium dioxide as additive are relatively high, the difference between the layer spacing and the ideal graphite layer spacing is the smallest, and the degree of ordering of carbon materials is the highest. The Raman spectroscopy results showed that the order degree of coal -based graphite prepared under different additives was significantly different, and the order degree of TXSC3, TXTC2 and TXIC3 coal-based graphite was the highest among the additives. Under the electron microscope, it is found that under the conditions of three additives, the scales, spherical and two shapes of coal-based graphite can be prepared separately. It can be seen from the specific surface area and pore size distribution data of coal-based graphite that they have similar low-temperature nitrogen adsorption-desorption isotherms.